A105 Forged Solid Rounds OD 130MM ASME A105 Boiler Steel Round Bar
A 105 is an ASTM steel forging specification mainly used for carbon steel forged piping
components. This type of carbon steel forging alloy involved is a low carbon, manganese and silicon containing
steel similar to AISI 1330, but with lower manganese content.
Chemical Composition of ASTM A105
Carbon: ≤0.35
Manganese: 0.60-1.05
Phosphorus: ≤0.35
Sulfur: ≤0.40
Silicon: 0.10-0.35
Copper: ≤0.40
Nickel: ≤0.40
Chromium: ≤0.30
Molybdenum: ≤0.12
Vanadium: ≤0.08
Mechanical Properties of ASTM A105
| Tensile Strength min. | Yield Strength min. | Elongation min. | Reduction of Area, min. | Hardness |
| MPa | ksi | MPa | ksi | % | % | HBW |
| 485 | 70 | 250 | 36 | 22 | 30 | 137-187 |
ASTM A105 carbon steel can be forged at temperatures in the range
of 2200 to 1700 F followed by quenching and tempering or
normalizing. The actual hot forging temperatures in closed die forging process will be decided by a number of factors, such as complexity
of the forged part.
The proper temperature of forging can only be checked at the
beginning of forging, higher temperature will probably cause
surface defects, such as mill scales, which will bring uneven
surface. And lower temperature will be not conducive to the plastic
deformation of C1045 carbon steel forged part.
A105 forgings are limited to a maximum weight of 4540 kg [10000
lb]. As stated in our quality manual, welding repair of defects in
ASTM A105 flanges or fittings is absolutely prohibited by
Metals-Piping(although it is permissible by the standard).
Heat Treatment
Heat treatment is not required except for ASTM A 105 carbon steel
forging. However, there are some exceptions that will require heat
treatment to improve its mechanical properties for better
application.
The typical heat treatment conducted for A105 carbon steel forgings
includes annealing(A), normalizing(A), normalizing and
tempering(NT), quenching and tempering(QT). Especially, normalizing
at approximate 950°C for 2.5 hours is often required by many
clients to eliminate possible internal stress in the forgings.
These materials are usually marked as “ASTM A105N”.
Machinability
Machinability of A105 carbon steel forging is good as for any of
the low alloy steels.
Applications
This ASTM specification covers carbon steel forgings for piping
applications such as flanges and fittings (45°eblow, 90° eblow, tee, coulping, etc)